著者
天藤 雅之 竹下 哲郎 中澤 崇徳 木村 英隆 安保 秀雄
出版者
The Iron and Steel Institute of Japan
雑誌
鉄と鋼 (ISSN:00211575)
巻号頁・発行日
vol.79, no.1, pp.98-104, 1993-01-01 (Released:2009-06-30)
参考文献数
14
被引用文献数
14 20

Room temperature creep behavior has been investigated for typical stainless steels (SUS304, SUS430, SUS410L). The mechanism of creep is discussed in comparison with creep data on a carbon steel (SM400).The results are summerized as follows:1) Stainless steels showed creep deformation at a stress around 0.2% proof stress. Though creep rate decreased monotonously with increase in time, deformation did not ceased even at a time 1000 h. The creep curve of SUS304 steel followed a logarithmic creep law.2) No creep was observed in steel SM400 below a critical strain rate at around 10-8S-1.3) The facts that interstitial free steels showed room temperature creep, and that SUS304 steel showed no creep at 300°C suggest that the suppression of creep can be attributed to the dynamic strain aging due to the interaction between dislocation and interstitial carbon and nitrogen atoms.

言及状況

外部データベース (DOI)

Yahoo!知恵袋 (1 users, 1 posts)

常温クリープはステンレスではオーステナイト系、 フェライト系ともに僅か起きるが、一般鋼はゼロ として差支えありません。 https://www.jstage.jst.go.jp/article/tetsutohagane1955/79/1/79_1_98/_pdf SM400に降伏応力より大きい295MPaを負荷する とクリープ変形は起きるが数時間で終わり、以降 は全く観察され ...

Twitter (1 users, 1 posts, 0 favorites)

知らなんだ。 おもしろ https://t.co/lfNN9wtVo2

収集済み URL リスト