著者

森 敬祐 真壁 朝敏 安藤 新二 井上 晋一

出版者

一般社団法人 日本高圧力技術協会

雑誌

圧力技術 (ISSN:03870154)

巻号頁・発行日

vol.58, no.1, pp.14-21, 2020

---

Fatigue crack growth tests of rolled magnesium alloy AZ31 were performed with a side-notch plate specimen under negative mean stress conditions. In the results of the present study, even if the experimental conditions were the same, the crack growth behavior varied depending on the condition of the specimen and depending on the microstructure. The local friction between large size and small size crystals and the shear deformation are expected to be related to the crack closure. The crack growth rate was affected by the crack opening stress. When the crack growth rate was lower level, the crack closure behavior worked due to the plastic deformation and the roughness of the fracture surface. There was local rough pattern which work as the shear lip at sides of the crack surface.