著者
須田 明彦 神取 利男 右京 良雄 曽布川 英夫 杉浦 正洽
出版者
公益社団法人日本セラミックス協会
雑誌
日本セラミックス協会学術論文誌 : Nippon Seramikkusu Kyokai gakujutsu ronbunshi (ISSN:18821022)
巻号頁・発行日
vol.108, no.1257, pp.473-477, 2000-05-01
被引用文献数
9 19

The surprisingly low temperature (〜323 K) synthesis of the ceria-zirconia solid solution upon milling ceria powder with zirconia mill and zirconia balls (in ethanol and/or water) was studied. Solid solutions up to 60 mol%ZrO_2 were obtained, whose formation was proved to result from solid phase reaction between ceria and zirconia powders, enhanced by contact stress (either shear or compressive one). Furthermore, the occurrence of large plastic deformation, breaking and mutual combining was found on the ceria powder before and after solid solution. The grain size of ceria-zirconia solid solution was ≨20 nm, which would cause on easy rearrangement of low diffusion atoms of cerium and zirconium to form the solid solution at such a low temperature. In addition, the possible existence of a solid solution for which the migration of the constituents is much faster (or the stability of the solid at the composition is much higher) than that of other composition, was suggested around 50 mol%CeO_2-50 mol%ZrO_2.
著者
右京 良雄 神取 利男 和田 重孝
出版者
公益社団法人日本セラミックス協会
雑誌
日本セラミックス協会学術論文誌 : Nippon Seramikkusu Kyokai gakujutsu ronbunshi (ISSN:18821022)
巻号頁・発行日
vol.101, no.1180, pp.1430-1431, 1993-12-01
被引用文献数
9 7

Si<sub>3</sub>N<sub>4</sub>-SiC particle composites constaining up to 30wt% SiC were sintered to a neary full density using gas pressure sintering and HIPing process (post-HIPing). Fine SiC powder with an average particle size of about 0.03μm, and Y<sub>2</sub>O<sub>3</sub> as sintering additive were used. Si<sub>3</sub>N<sub>4</sub>-30wt% SiC sintered composite with a strength of about 700MPa at 1400°C was obtained by post-HIPing.