- Ishizuka Shogo Yamada Akimasa Islam Muhammad Monirul Shibata Hajime Fons Paul Sakurai Takeaki Akimoto Katsuhiro Niki Shigeru
- 出版者
- American Institute of Physics
- 雑誌
- Journal of applied physics (ISSN:00218979)
- 巻号頁・発行日
- vol.106, no.3, pp.034908, 2009-08
- 被引用文献数
- 144 57
The systematic variations in the structural, optical, and electrical properties of polycrystalline Cu(In,Ga)Se2 (CIGS) thin films with Na doping level were investigated. Precise control of the Na concentration in CIGS films was demonstrated using alkali-silicate glass thin layers of various thicknesses deposited on substrates prior to CIGS growth. The CIGS grain size was observed to decrease with increasing Na concentration, although the surface morphology became smoother and exhibited a stronger (112) texture, which has been demonstrated consequence of larger grain size. The Ga composition gradient in the CIGS films was found to become large due to the presence of Na during growth, which in turn led to a decrease in the nominal band gap energy. Variations in the photoluminescence spectra and electrical properties suggested that the formation of an acceptor energy state, which may originate from OSe point defects, was enhanced in the presence of Na. This result suggests that not only Na, but also the presence of O in combination with Na contributes to the compensation of point defects and enhances p-type conductivity in CIGS films.
1 0 0 0 OA Favorable electronic structure for organic solar cells induced by strong interaction at interface
- 著者
- Wang Shenghao Sakurai Takeaki Hao Xia Fu Wei Masuda Shigeru Akimoto Katsuhiro
- 出版者
- American Institute of Physics
- 雑誌
- Journal of applied physics (ISSN:00218979)
- 巻号頁・発行日
- vol.114, no.18, pp.183707, 2013-11
- 被引用文献数
- 8 2
To clarify the role of buffer layer in organic solar cells (OSCs), the electronic properties of bathocuproine (BCP)/Mg interface were systematically investigated by using ultraviolet photoemissions spectroscopy, high-resolution X-ray photoemission spectroscopy, angle-resolved X-ray photoemission spectroscopy and near-edge X-ray absorption fine structure (NEXAFS) spectroscopy. The results show there are gap states at the interface, which are caused by the interaction between BCP and Mg. The formation of Mg-N bond was found at the interface. The NEXAFS measurements show that BCP molecules for 1-2 monolayers are lying-down on the substrate, whereas orient randomly for thick BCP layer. It was supposed that the gap states and the highly-ordered orientation of thin BCP layer are the reasons for improving the performance of OSC with BCP buffer layer and low work function metal cathode.