下尾 聰夫 早津 俊秀 成澤 雅紀 武田 道夫 市川 宏 瀬口 忠男 岡村 清人
出版者
公益社団法人日本セラミックス協会
雑誌
日本セラミックス協会学術論文誌 : Nippon Seramikkusu Kyokai gakujutsu ronbunshi (ISSN:18821022)
巻号頁・発行日
vol.101, no.1180, pp.1379-1383, 1993-12-01
被引用文献数
10 10

The pyrolysis of the low oxygen (1.7% O) SiC fiber prepared by the electron-irradiation curing method has been investigated. The pyrolytic rate was measured with a thermobalance in Ar at temperatures from 1673 to 1973K. The pyrolyzed fiber was examined by X-ray diffraction, SEM observation, specific resistance measurement and tensile test. Lowering of oxygen content in the fiber was found to be effective for the suppression of pyrolysis. The pyrolyzed fiber was composed of β-SiC and amorphous carbon. The growth and coarsening of SiC crystals were observed on the skin of the fiber, while the core was smooth and remained in the microcrystalline state. The tensile strength of the fiber, which was heated at 1973K for 3.6ks, retained 34% of that of the original fiber. The strength was correlated closely with the size of the β-SiC crystal in the fiber.

言及状況

外部データベース (DOI)

Wikipedia (1 pages, 1 posts, 1 contributors)

編集者: たかながさえあ
2020-06-15 10:53:48 の編集で削除されたか、リンク先が変更された可能性があります。

収集済み URL リスト