著者

太田 昭彦 渡辺 修 松岡 一祥 志賀 千晃 西島 敏 前田 芳夫 鈴木 直之 久保 高宏

出版者

社団法人溶接学会

雑誌

溶接学会論文集 : quarterly journal of the Japan Welding Society (ISSN:02884771)

巻号頁・発行日

vol.18, no.1, pp.141-145, 2000-02-05

参考文献数

18

被引用文献数

22

---

The fatigue strength of developed box welds was improved about two times of the conventional box welds. The improved welds used the low transformation temperature welding material which contains 10% Cr and 10% Ni. The expansion of the developed welding material was 0.55% due to the transformation from austenite to martensite. This expansion induced the compressive residual stress around welds. On low stress range condition, the stress ratio effect by this compressive residual stress avoids the fatigue crack initiation at the weld toe. On high stress range condition, the fatigue crack initiated from weld toe and the fretting was observed on the fractured surface. While in the conventional welds, no trace of fretting was observed.