著者

Morimoto Masahiro Koshiba Yasuko Misaki Masahiro Ishida Kenji

出版者

Institute of Physics

雑誌

Jpn. J. Appl. Phys. (ISSN:00214922)

巻号頁・発行日

vol.54, no.4, 2015-03-27

被引用文献数

8

---

We have investigated the pyro- and piezoelectric properties of polyurea spin-coated films with thermal and chemical stability and their performance as infrared sensors. The piezoelectric coefficient d<inf>33</inf>was measured by a laser Doppler vibrometer to be 23.5 pC/N. This coefficient increased with the poling electric field up to around 75 MV/m, suggesting that the polyurea dipole is aligned by applying an electric field greater than 75 MV/m. When a triangular thermal wave was applied, a square-wave pyroelectric current was observed and the pyroelectric coefficient measured to be 5.11 µC/(m²·K). The infrared sensor performance of the polyurea thin film was examined by measuring the voltage sensitivity to infrared irradiation. The obtained result of 70.4 V/W at 1 Hz is consistent with the results calculated from the measured pyroelectric coefficient. Our findings suggest that the performance of the sensor may be improved by increasing the pyroelectric coefficient of the polyurea films.