- 著者
-
熊澤 孝夫
中川 渡
鶴丸 秀一
- 出版者
- 一般社団法人 電気学会
- 雑誌
- 電気学会論文誌A(基礎・材料・共通部門誌) (ISSN:03854205)
- 巻号頁・発行日
- vol.125, no.10, pp.828-834, 2005
- 被引用文献数
-
6
9
Bow-tie tree(BTT) generated from contaminant, <i>e.g.</i>, metal, carbon, amber(over cured resin) or void is a deterioration factor of XLPE cable. In particular, BTT in contact with inner or outer semi-conductive shield could significantly lower residual AC breakdown voltage of HV power cable. To evaluate influence of water and ion diffusion on generation and progress of BTT, we investigated relationship between water content of XLPE and the generation of BTT by various accelerated aging. The number of BTT in XLPE samples with accelerated aging under open condition, involving evaporation of water in which samples were immersed, was very large compared with closed condition. Furthermore, when samples were intermittently immersed in water, the number of BTT in samples was large compared with samples immersed continuously. In these experiments the generation of BTT seemed to have nothing to do with changes in water content before and after accelerated aging. Therefore, it was suggested that diffusion of ions rather than water in XLPE played an important role in the generation of BTT.