The purpose of this study is the development of simultaneous processing of diffusion bonding and surface nitriding. Carbon steel was used as the base material. The surface was nitrided to a 20-μm-thick titanium foil. The sample was arranged in the order of carbon steel, titanium foil, and Al2O3 powder (diameter=1 μm) and placed in N2 gas in a furnace to undergo simultaneous diffusion bonding and surface nitriding. These processes were carried out at a processing temperature T of 1100~1250 K and processing pressure P of 0.5 MPa (processing time=4.8 ks). Because no defect was observed in the bonded interface, it was confirmed that a sufficiently suitable joint can be obtained under these processing conditions. The surface hardness was observed to increase with the increase in processing temperature; it reached approximately HV1600 at 1250 K. The surface of the titanium foil, which had been simultaneously processed at 1250 K, consisted of a single phase of TiN. The results of the ball-on-disc-type wear test revealed that the surface, which had been processed at 1250 K, was hardly worn by the TiN layer.