Aragonite-type calcium carbonate was synthesized from calcined scallop shell using carbonates of orthorohombic structure (such as SrCO3) as seeds, by bubbling CO2 at ambient temperature. The products were examined by FTIR, SEM, EPMA, and XRD. The addition of SrCO3 increased aragonite content in the products, but BaCO3 and PbCO3 did not play the role of seed crystals due to the difference of their lattice parameters to those of aragonite, whereas lattice parameters of SrCO3 are the most similar to them. With increasing SrCO3 -addition, formation of aragonite was accelerated to a limit in the amount. Light calcium carbonate rich in aragonite was formed in agglegates consisting of needle-like crystals with large specific surface areas.

著者

笹木 圭子 本郷 大 恒川 昌美

出版者

一般社団法人 資源・素材学会

雑誌

資源と素材 (ISSN:09161740)

巻号頁・発行日

vol.114, no.10, pp.709-713, 1998-08-25 (Released:1999-10-01)

---

Aragonite-type calcium carbonate was synthesized from calcined scallop shell using carbonates of orthorohombic structure (such as SrCO3) as seeds, by bubbling CO2 at ambient temperature. The products were examined by FTIR, SEM, EPMA, and XRD. The addition of SrCO3 increased aragonite content in the products, but BaCO3 and PbCO3 did not play the role of seed crystals due to the difference of their lattice parameters to those of aragonite, whereas lattice parameters of SrCO3 are the most similar to them. With increasing SrCO3 -addition, formation of aragonite was accelerated to a limit in the amount. Light calcium carbonate rich in aragonite was formed in agglegates consisting of needle-like crystals with large specific surface areas.