著者
菊池 賢靖 神谷 修 齋藤 省律 熊谷 一男
出版者
日本素材物性学会
雑誌
素材物性学雑誌 (ISSN:09199853)
巻号頁・発行日
vol.11, no.2, pp.12-20, 1998-12-30 (Released:2010-10-28)
参考文献数
9
被引用文献数
5 5

Beginning of the repeatedly wear, severe wear condition of high wear rate becomes predominate. The wear rate decreases with time and the wear condition changes to a mild wear. After that, a wear becomes hardly advance and becomes stable condition. An oxide film forms at a worn surface and the surface geometry becomes smooth. That condition is called “running-in”. The transition mechanism from severe to “running-in” is important for constant operation of the machine that has a mobile components contacting among metals. A drying repeated wear test of a pin on disk was studied under unlubrication condition in this report. Also, a change of a running-in process in magnetic field has been studied. The results are reported as follows.
著者
熊谷 一男
出版者
一般社団法人日本機械学会
雑誌
日本機械学會論文集. A編 (ISSN:03875008)
巻号頁・発行日
vol.46, no.408, pp.894-900, 1980-08-25
被引用文献数
1

0. 02% C軟鋼線の, 降伏応力以下の応力を加えたひずみ時効において(1)応力は, 降伏応力の増加を最大10%促進する. (2)みかけの活性化エネルギは, 約1kcal/mol増加する. (3)応力による時効促進への寄与率は, ひずみ硬化が約20%, 新たに導入された転位への微細析出物の析出が約3%で, 促進の主たる要因は, 応力による侵入形固溶原子の拡散ならびに析出の促進と考えられることを示した.