著者

牧 涼介 彭 沢亮 福原 実 草野 圭弘

出版者

一般社団法人 粉体粉末冶金協会

雑誌

粉体および粉末冶金 (ISSN:05328799)

巻号頁・発行日

vol.69, no.10, pp.409-414, 2022-10-15 (Released:2022-10-15)

参考文献数

11

被引用文献数

1

---

Bizen stoneware is produced by firing shaped green clay in a firewood kiln at around 1200°C. The brownish and blackish colors that appear on the stoneware surface in a firewood kiln do not appear on stoneware heated in an electric furnace. The brownish color was found to be caused by the formation of single crystalline, branched, dendritic, Al-substituted ε-Fe2O3 particles. Composite particles consisting of Al-substituted ε-Fe2O3 and Fe-substituted spinel solid solution also formed on the stoneware surface. In this study, we successfully prepared brownish samples that were similar in color to Bizen stoneware by annealing at 1200°C for 2 h in air after heating Bizen clay pellets with K2CO3 at 1230°C under a 10 vol% CO and 90 vol% Ar gas mixture in an electric furnace instead of firing in a firewood kiln. Dendritic hematite particles also formed on the reproduced samples. The blackish color on Bizen stoneware fired in a firewood kiln was caused by the formation of augite [(Ca,Mg,Fe)2Si2O6], which was produced by a reaction between the Bizen clay and firewood ash.