著者

葛巻 星 西岡 宣泰 藤代 史 武部 博倫

出版者

一般社団法人 資源・素材学会

雑誌

Journal of MMIJ (ISSN:18816118)

巻号頁・発行日

vol.137, no.11, pp.110-115, 2021-11-30 (Released:2021-11-30)

参考文献数

27

被引用文献数

2

---

A stabilized zirconia oxygen probe was used to measure the oxygen partial pressure (OPP) at an electrode submerged in a copper slag melt at 1300 ℃. The OPP was controlled in the range of 10−10–10−5 atm owing to the presence or absence of a powdered carbon layer on the slag melt using a high-purity alumina crucible in argon (Ar) gas flow. Under suppression of magnetite formation at an OPP of approximately 10−10 atm, the viscosities of the copper slag and FeO-Fe2O3-SiO2-Al2O3 slag melts were measured between 1200 ℃ and 1300 ℃. The obtained values were in the range of 1.0×102–7.8×102 mPa・s. The dependences of total Fe/SiO2 mass ratio and Al2O3 concentration on viscosity were qualitatively interpreted from the aluminosilicate network structure viewpoint.