High pressure synthesis was performed on 123 and 124 phases in Y-Ba-Cu-O system under a pressure of 3GPa at 950°C. Lattice parameters and superconducting properties changed with an annealing duration under pressure in 123 phase with oxygen content X=7. The 123 product obtained from raw materials with X=8.5 had a tetragonal lattice with a=c/3=3.87A. Its real oxygen content could be estimated to be 7.3 from the lattice parameter, Raman spectroscopy, and also Rietveld analysis. The product seemed to be semiconductor containing a small amount of superconductor. 124 phase was obtained by a reaction at 950°C with its successive annealing at 700°C under 3GPa adjusting oxygen content of raw material to the exact composition of the product.

著者

水田 博之 芝崎 靖雄 延谷 宏治 金丸 文一

出版者

公益社団法人 日本セラミックス協会

雑誌

窯業協會誌 (ISSN:00090255)

巻号頁・発行日

vol.90, no.1043, pp.355-362, 1982-07-01 (Released:2010-04-30)

参考文献数

5

---

0.12K2O・0.48PbO・0.40ZnO・0.15Al2O3・1.70SiO2(mol) の基本組成を持つ基礎釉及び基本組成にTiO2(5wt%) とNH4VO3(3wt%) を単独または同時に加えた組成の釉について結晶化及び虹彩現象の研究を行った.1150°-1250℃の温度範囲で溶融後徐冷すると基礎釉及びV添加釉ではZn2SiO4の結晶が析出するが, Ti添加釉ではZn2SiO4とZn2TiO4の結晶が析出した. TiとVを同時添加した釉ではルチル型 (TiO2) が主として析出し鮮やかな虹彩を示した. この虹彩現象は葉片状に集合した薄板状ルチル型 (TiO2) の析出によって引き起こされるが, Zn2TiO4やZn2SiO4の析出は逆に虹彩現象を弱めた. 析出結晶相の同定には, 実体顕微鏡, 走査型電子顕微鏡, 分析電子顕微鏡やX線回折装置を用い, 析出結晶と虹彩現象との関連性を詳しく議論した.