著者

堀田 慎一 鈴木 佳司 渡辺 幹男 本間 英夫

出版者

The Surface Finishing Society of Japan

雑誌

表面技術 (ISSN:09151869)

巻号頁・発行日

vol.44, no.10, pp.831-835, 1993-10-01 (Released:2009-10-30)

参考文献数

9

被引用文献数

3 3

---

Various factors influencing the adhesion between glass and electroless nickel plated films were investigated. In terms of the film, it was found that the use of glycine as a complexing agent resulted in films that exhibited good adhesion. Adhesive strength also increased at lower pH and lower plating bath temperature. In terms of pretreatment, etching was important to improving adhesion. Adhesive strength was greatest when the glass was first etched with sodium hydroxide, next etched with hydrofluoric acid and then treated with methylate. Adhesion was also increased by decreasing the level of dissolved oxygen in the catalyzing treatment solution and plating bath.