著者
山田 豊 長谷部 次教 柳谷 知之 直原 和哲 石塚 正之 安原 征治 石原 守
出版者
公益社団法人 低温工学・超電導学会
雑誌
低温工学 (ISSN:03892441)
巻号頁・発行日
vol.28, no.2, pp.86-91, 1993-02-25 (Released:2010-02-26)
参考文献数
12
被引用文献数
3 7

Superconducting properties of Bi-Pb-Sr-Ca-Cu-O superconducting bulk fabricated by intermediate cold isostatic pressing (C. I. P.) process have been investigated, and heat leakage per a bulk lead pair from 77K to 4.2K has been evaluated. The critical current density of the tubular bulk, approximately inner diameter 10-30mm and 200mm long, was indicated more than 1, 000A/cm2 at 77K under self-magnetic field, and at 4.2K was indicated as about 2, 000A/cm2 under 15T. The reasons for improvement of Jc are the formation of high Tc single phase and highly aligned microstructure of the bulk. The heat leakage per a pair of the bulk leads from 77K to 4.2K has been measured to be 0.16W at DC 800A and considered to be less than one-tenth of that of 800A-class conventional gas-cooled current leads.