著者

Kazuki Akamatsu Keigo Imamura Shin-ichi Nakao Xiao-lin Wang

出版者

The Society of Chemical Engineers, Japan

雑誌

JOURNAL OF CHEMICAL ENGINEERING OF JAPAN (ISSN:00219592)

巻号頁・発行日

vol.55, no.8, pp.255-261, 2022-08-20 (Released:2022-08-20)

参考文献数

36

被引用文献数

1

---

We developed a membrane reactor integrating dimethoxydimethylsilane (DMDMS)-derived hydrogen-selective silica membranes with Rh/Al2O3 catalysts and produced high-purity hydrogen from simulated biogas by operating the reactor under pressure on the reaction side while maintaining ambient pressure and excluding sweep gas that has often been used on the permeate side. We investigated changes in the performance of the DMDMS-derived membrane when exposed to pressurized hydrothermal conditions. The results indicated that pressure had a nonnegligible effect on membrane performance and led to a more severe decline in hydrogen permeance compared with exposure under similar hydrothermal conditions but at 0.1 MPa pressure. Although the performance of the DMDMS-derived membrane decreased, we developed a membrane reactor and operated it for hydrogen production. For the various pressures (0.6–1.0 MPa) and temperatures (500–600°C) tested, the conversions exceeded those in the packed-bed reactor, and high hydrogen purity was achieved without the use of sweep gas. Specifically, 55% conversion with 94% hydrogen purity was achieved when the membrane reactor was operated at 0.6 MPa and 600°C.