著者

Park Yuong Chul Park D. S. Lee Gyun Ghung 古屋 泰文

出版者

一般社団法人日本機械学会

雑誌

年次大会講演論文集

巻号頁・発行日

vol.1, pp.347-348, 2001

---

Al alloy matrix composite with TiNi shape memory fibers as reinforcement has been fabricated by hot pressing to enhance the mechanical properties. The smartness of the composite is given due to the shape memory effect of the TiNi fiber which generates compressive residual stress in the matrix material when heated after being prestrained. It showed that the yield stress at 90℃ was higher than that of the room temperature. Especially, the tensile Strength of this composite increases with increasing amount of prestrain, and it also depends on the volume fraction of fiber and heat treatment. Comparison between theoretical estimation and experimental data showed almost good correlation by introducing non-linear FEM analysis.

著者

Park Yuong Chul Park D. S. Lee Gyun Ghung 古屋 泰文

出版者

一般社団法人 日本機械学会

雑誌

年次大会講演論文集

巻号頁・発行日

vol.1, pp.347-348, 2001

---

Al alloy matrix composite with TiNi shape memory fibers as reinforcement has been fabricated by hot pressing to enhance the mechanical properties. The smartness of the composite is given due to the shape memory effect of the TiNi fiber which generates compressive residual stress in the matrix material when heated after being prestrained. It showed that the yield stress at 90℃ was higher than that of the room temperature. Especially, the tensile Strength of this composite increases with increasing amount of prestrain, and it also depends on the volume fraction of fiber and heat treatment. Comparison between theoretical estimation and experimental data showed almost good correlation by introducing non-linear FEM analysis.