We investigated the influence of different curing modes on the mechanical properties and wear behavior of dual-cure provisional resin-based composites (DCPRs). Three DCPRs and a self-curing bis-acryl provisional resin-based composite were used. Flexural strength (σF), elastic modulus (E), resilience (R), and fracture toughness (KIC) were measured. The specimens were fabricated with and without light irradiation, stored in distilled water at 37°C for 24 h, and subjected to 5,000 or 10,000 thermal cycles. For sliding impact wear testing, 12 specimens were prepared with and without light irradiation. The maximum facet depth and volume loss were determined using a noncontact profilometer. Some of the mechanical properties and wear behavior of DCPRs are affected by light irradiation. This study indicated that proper light irradiation is important in polymerization process of the DCPRs to enhance the wear resistance and some mechanical properties.

著者

Ryosuke Murayama Yuko Nagura Kabun Yamauchi Nobuyuki Moritake Masayoshi Iino Ryo Ishii Hiroyasu Kurokawa Masashi Miyazaki Yumiko Hosoya

出版者

Nihon University School of Dentistry

雑誌

Journal of Oral Science (ISSN:13434934)

巻号頁・発行日

pp.17-0256, (Released:2018-07-09)

参考文献数

40

被引用文献数

5

---

We used optical coherence tomography to examine the effect of a coating material containing surface reaction-type pre-reacted glass-ionomer (S-PRG) filler on primary enamel demineralization in 18 extracted human primary teeth. The pulp was removed, and each tooth was ultrasonically cleaned with distilled water. Six teeth were treated with 0.1-M lactic acid buffer solution (De group). In the second group (n = 6), a thin film of coating material was applied before demineralization (PRG group). A third group (Control group; n = 6) was maintained in artificial saliva. Using optical coherence tomography, we measured peak signal intensity (dB) and width at 1/e2 (µm) at predetermined locations on the enamel surface and calculated integrated values. All data were analyzed with ANOVA and the Tukey-Kramer test (α = 0.05). Although changes in integrated values differed between groups, there was a small but significant increase in the Control group and a small but significant decrease in the De group. In the PRG group, integrated values were significantly higher at 7 days after the start of the experiment and significantly increased thereafter. Our findings indicate that a coating material containing S-PRG fillers may prevent primary enamel demineralization.