Sulfur-added vanadium pentoxide (S-V2O5) powder prepared using our method was applied to the cathode active material used in magnesium rechargeable batteries. The preparation of S-V2O5 from a sulfur and vanadium pentoxide mixture was done with low-temperature plasma generated using carbon felt and 2.45-GHz microwave (CF-MWP). The S-V2O5 structure was investigated using XRD, XPS, Raman spectroscopy, and DRS-FTIR. Results revealed that the S-V2O5 particle surface contains sulfur atoms and that its structure is amorphous, like xerogel, although the bulk preserved the same structure as that of V2O5 crystal. Charge-discharge tests for S-V2O5 showed exceedingly high specific capacity of 300 mAhg−1, which far surpasses that of V2O5 (160 mAhg−1). The cycle performance of S-V2O5 (300 mAhg−1 after 20 cycles) was also more stable than that of V2O5 (70 mAhg−1 after first cycle). Moreover, the discharge voltage and the specific capacity did not degrade under any discharge rate condition from C/2 to C/10.

言及状況

外部データベース (DOI)

Twitter (12 users, 15 posts, 18 favorites)

I本氏とK原氏、どっちが立場がおエライさんなのか解らなくなってた。今回の発表ではK氏手動、正極材料はI氏 https://t.co/himlWCcrJi … なだけで、埼TECでどっちが上司とか先輩とかではないのかも。(続)
https://t.co/UGvghXbjwj 関連記事 常温で安全 県産業技術総合センター開発 https://t.co/y1Jm7wqFP1 関連論文 マグネシウム二次電池正極材料としての硫黄を添加した五酸化バナジウムの電極特性 https://t.co/mAupudWobj
マグネシウム二次電池正極材料としての硫黄を添加した 五酸化バナジウムの電極特性 https://t.co/K4soF4Gb4S
1 1 https://t.co/CioquznG3l
これ https://t.co/himlWBUQRK の延長の筈なのでこれを使った正負極間のアレをあそこがやてるので多分1社はまずおそらくあそこでビンゴでしょう。https://t.co/L3mY1aPenC @SAW_saw_a_saw

収集済み URL リスト