- 著者
-
小山 元道
秋山 英二
津﨑 兼彰
- 出版者
- 一般社団法人 日本鉄鋼協会
- 雑誌
- 鉄と鋼 (ISSN:00211575)
- 巻号頁・発行日
- vol.100, no.9, pp.1132-1139, 2014 (Released:2014-08-31)
- 参考文献数
- 36
- 被引用文献数
-
4
Al effects on strain aging and resistance against hydrogen embrittlement were examined in Fe-18Mn-0.6C-based twinning-induced plasticity steels deformed at different strain rates. The Fe-18Mn-0.6C steel showed hydrogen-induced fracture when it had been pre-deformed at a strain rate of 1.7×10–6 s–1. The hydrogen-induced fracture was suppressed by increasing strain rate and increasing Al content. From the viewpoint of material strengthening by strain aging, we found two important factors improving the resistance to the hydrogen embrittlement; (1) suppression of dynamic strain aging by increasing strain rate and Al content, and (2) suppression of static strain aging under loading by the Al addition.