著者
原勢 二郎 太田 国照 清水 亮 竹下 哲郎
出版者
社団法人日本鉄鋼協会
雑誌
鉄と鋼 (ISSN:00211575)
巻号頁・発行日
vol.76, no.9, pp.1520-1527, 1990
被引用文献数
2 7

Orientation distribution in the 17%Cr stainless steel rough rolled with inter-pass time of 10s (specimen A) and 30s (specimen B) respectively were investigated utilizing SEM-ECP (selected area electron channeling pattern).<BR>Large colonies, groups of grains with the same orientation, of {100} <011>orientation are found in the specimen A after rough rolling. It is proposed to be formed by the poor static recrystallization during rough rolling due to the short inter-pass time and the suppression effect of static recrystallization caused by the &alpha;-&gamma; transformations immediately after the final pass of the rough rolling.<BR>Large ridging is observed in the cold rolled and annealed specimen A.<BR>The cause of the large ridging is considered to be due to the large colonies of {100} <011> orientation inherited from the rough rolled stage and scattered asymmetrically along the central line of the specimen thickness.

言及状況

外部データベース (DOI)

Twitter (1 users, 1 posts, 0 favorites)

こんな論文どうですか? 17%Crステンレス鋼板の結晶方位分布に及ぼす粗圧延工程の圧延パス間時間の影響(原勢 二郎ほか),1990 https://t.co/hWf8UXZvng Orientation distribution in the 17…

収集済み URL リスト