To control the amount of solute in cell walls of solution impregnated wood using the conditioning process, the mechanisms of solute diffusion into the cell walls and of solvent evaporation from wood under the process were verified. The effect of relative humidity (RH) on temporal variability of swelling, shrinkage, and mass of wood impregnated with an aqueous solution of polyethylene glycol (PEG1540) was examined. The impregnated wood specimen swelled under the conditioning at the RH over 75%. The specimen was indicated to swell when the amount of the PEG polymers in the cell walls increase in this RH range. On the basis of this indication, the temporal variability of increasing rate of the polymers in the cell walls and of evaporating rate of water from the specimen under the conditioning was well explained by the mechanisms of the solute diffusion and the solvent evaporation, respectively. In the RH range, the increasing amount of the polymers in the cell walls increased with the evaporating amount of the water, which increased with the decrease in the RH. These results were supported by the mechanisms of the solute diffusion and the solvent evaporation, respectively. The diffusion mechanism also supported the effect of the history of the RH on the polymer amount in the cell walls throughout the conditioning and subsequent drying in a vacuum. It was concluded from these findings that the solute diffusion into cell walls is able to be controlled by the surrounding vapor pressure of solvent when the polymers (PEG1540) and water are employed as the solute and solvent, respectively.

著者

三木 恒久 高倉 章雄 山口 克彦

巻号頁・発行日

2002-04

---

鉱物や化石燃料等の埋蔵資源は年々減少して枯渇の危機が近づいており、また、これらを原料とした製品が廃棄される場合は、産業廃棄物として扱われ、特にプラスチック系材料の焼却では有害ガス等が発生するため、今日深刻な環境問題を引き起こしている。 本研究では、石油系の接着剤等を一切使用せずに木材の構成要素のみに注目して、木材粉末を固形化する技術を開発し、環境・人間にやさしい任意形状の木質製品を製造することを目的としている。そのための基礎的実験として、木材粉末の圧粉成形および押出し成形を行い、最適固形化条件および押出し成形時の木材粉末の流動特性を明らかにした。そして、木材粉末を原料とした複雑形状部品を製造するための技術として、射出成形に代表されるニヤネットシェイプ成形の可能性とその問題点について検討した。京都工芸繊維大学環境科学センター報「環境」第14号 2002-04 pp.36-41