Amorphous silicon nitride powder (particle size: 0.04μm) obtained by the vapor phase reaction of Si(CH3)4-NH3 system was compacted into pellet and heat-treated in N2 to investigate the crystallization behavior. The amorphous powder crystallized to 100% α-Si3N4 by the heat treatment for 1h at 1550°C. The equiaxed crystalline particles having the size of 1-2μm were obtained when powder was compacted, whereas acicular particles were produced when powder was not compacted. When Si3N4 powder was used as powder bed which covered pellet, the crystalline particles grew extensively and the crystallinity increased with a decrease in the packing fraction of particles in pellet. The heat-treated powder with a low crystallinity consisted of fine amorphous particles and coarse crystalline particles. The crystallization seemed to proceed by a vapor phase growth mechanism, in which SiO vapor takes part as silicon carrier between amorphous particles and crystalline ones. When BN powder was used as powder bed, the crystallization and grain growth were retarded, and the crystal phase contained a small amount of β-Si3N4. Crystallization inhibitor, e. g. boron oxide, may have penetrated into pellet from BN powder.

著者

北條 純一

出版者

九州大学

雑誌

特定領域研究

巻号頁・発行日

2008

---

(1)セラミックス技術の公開いままでの調査を基礎として、それぞれの技術革新の歴史的展開を分析し、その技術展開の必然性をまとめ、将来の技術発展に貢献する知識基盤の集大成として国際セラミックス総合展2009に参加し、セラミックスアーカイブズについて出展した。関連分野の研究者から活発な質問を受け、本研究が高く評価されている事を実感でき、今後の研究の進め方について大いに役立つものであった。また、第5回シンポジウムでセラミックスアーカイブスとして最後のまとめについて講演を行った。(2)インターネット博物館セラミックスに関するバーチャルな博物館を設立するため、これらの成果を日本セラミックス協会の「セラミックス博物館」として公開した。http://www.ceramic.or.jp/museum/(3)研究成果の出版アーカイブズ出版小委員会を2月に開催、出版方針について検討し、英語版として出版することとした。