To clarify the wear resistance and seizure resistance of the vegetable oils with anti-wear additives of Dibenzyl-Disulfide (DBDS) and Phosphonic Acid-Dibutyl (DBPo), the four-ball tests were carried out under dip-feed lubrication using Soda-type four-ball machine. The width of the wear scar on the stationary balls lubricated with the vegetable oils containing DBPo additive was smaller than that without the additive, and was smaller than that containing DBDS additive. The seizure resistance of the vegetable oils with DBDS additive increased in following order : Turbine oil<Rapeseed oil<Soybean oil<Corn oil. On the other hand, the seizure resistance of the vegetable oils with DBPo additive increased in the following order : Turbine oil<Soybean oil<Corn oil<Rapeseed oil. The DBPo additive showed significant improvements in seizure resistance compared with DBDS additive.

著者

灘野 宏正 中迫 正一 河野 正来 南 一郎 山口 博幸

出版者

一般社団法人 日本機械学会

雑誌

日本機械学会論文集 C編 (ISSN:03875024)

巻号頁・発行日

vol.70, no.690, pp.554-559, 2004

---

To clarify the wear resistance and seizure resistance of the vegetable oils with anti-wear additives of Dibenzyl-Disulfide (DBDS) and Phosphonic Acid-Dibutyl (DBPo), the four-ball tests were carried out under dip-feed lubrication using Soda-type four-ball machine. The width of the wear scar on the stationary balls lubricated with the vegetable oils containing DBPo additive was smaller than that without the additive, and was smaller than that containing DBDS additive. The seizure resistance of the vegetable oils with DBDS additive increased in following order : Turbine oil<Rapeseed oil<Soybean oil<Corn oil. On the other hand, the seizure resistance of the vegetable oils with DBPo additive increased in the following order : Turbine oil<Soybean oil<Corn oil<Rapeseed oil. The DBPo additive showed significant improvements in seizure resistance compared with DBDS additive.

著者

灘野 宏正 中迫 正一 河野 正来

出版者

一般社団法人日本機械学会

雑誌

日本機械学會論文集. C編 (ISSN:03875024)

巻号頁・発行日

vol.61, no.592, pp.4763-4768, 1995-12-25

被引用文献数

2

---

To clarify the seizure resistance of stainless steel balls of which the surface layer was thermally diffused after being Sn-plated, a four-ball test was carried out with grease lubrication. From the tests, the following results were obtained. The diameter of the wear scar of the ball lubricated with the grease containing a molybdenum disulfide additive was smaller than that of the ball lubricated with the grease without the additive, and the diameter of the wear scar increased with increasing concentration of the additive. The load at the incipient stage of seizure of the ball of which the diffused surface layer was about 6 μm thick was 2〜4 times larger than that of the ball without the diffused surface layer. Further, it was found that the seizure resistance of the balls could be estimated from the critical surface temperature and that the critical temperature increased with increasing concentration of the additive.