The recent research circumstances of photocatalytic overall splitting of H2O and the membrane separation of H2 and O2 for constructing the hydrogen production system by applying photocatalytic H2O splitting are introduced. Here, the principle of photocatalytic H2O splitting and photocatalysts for the reaction are explained on the historical aspect. Furthermore, the photocatalysts with high photocatalytic ability to the reaction, not only the photocatalysts and photocatalytic systems work under solar irradiation but also those show high efficiency are introduced. Incorporating gas separation membranes into the photocatalytic reactor leads to a safe and energy-efficient hydrogen production process. Since any research of application of gas separation membrane to this purpose has not been found in the literature, our research is introduced. The goal performance that the membrane should achieve to produce safe H2 and O2 streams have been determined by a simple model of a membrane module. Permeability and selectivity of H2 over O2 for silica membranes, carbon membranes, and polyimide membranes have been examined in a temperature range from 35 to 100 °C. Some silica membranes have passed the goal at 100 °C for a wet mixture of H2/O2(2/1).

著者

今村 速夫 酒多 喜久

出版者

山口大学

雑誌

基盤研究(C)

巻号頁・発行日

2008

---

ボールミリングによるナノ複合化によって、Mg水素化物を活性化して水素の放出過程を促進させることを材料開発のコンセプトに、Sn/MgH_2やSiC/MgH_2を検討した。MgH_2の微結晶中に高分散したSnやSiCのナノコンポジットでは、複合効果が発現して水素の放出温度が低下した。Sn/MgH_2系では、ナノ複合化の結果、MgH_2の水素放出温度が473K近くまで低下した。これはSnによるMgH_2からの水素放出過程における動力学的な促進効果よりも水素化物の熱力学的な不安定化に起因することがわかった。TDS(熱放出スペクトル),DSC(示差熱量分析),TG(熱重量分析)測定よりMg複合系では、複合化の結果少なくとも二種類の水素種が存在することがわかった。