In order to recover trace of platinum (Pt) from hydrochloric acid (HCl) leaching solution of Cobalt-Rich Crust (CRC), the absorption properties of four kinds of seaweeds (Undaria pinnatifida, Laminaria angustata, Enteromorpha linza and Gloiopeltis tenax) and activated carbon were studied. At first, their adsorption abilities for Pt ion as well as selective adsorption properties for other coexisting metal ions contained in CRC (including iron (Fe), manganese (Mn), cobalt (Co), nickel (Ni) and copper (Cu)) were investigated by using artificial solutions. Finally, the application to CRC HCl leaching solution was also carried out. The results showed that all seaweeds achieved their best Pt adsorption capacity only at pH 2, whereas activated carbon possessed a high Pt adsorption ability over a wide pH range from pH 0 to 6 as well as in HCl solution up to 3 mol/L. Regarding the CRC leaching solution obtained by 0.5 mol/L HCl and 1 vol.% hydrogen peroxide (H2O2), 46.9% and 100% Pt was recovered by Enteromorpha linza and activated carbon, respectively. It was found that seaweed and activated carbon are both effective adsorbents for recovering Pt from HCl leaching solution of CRC.

著者

DODBIBA Gjergj 藤田 豊久

出版者

東京大学

雑誌

挑戦的萌芽研究

巻号頁・発行日

2010

---

本研究では金属液体として金属ガリウムを使用し、分散させる強磁性粒子には数百nmの粒子径で温度の上昇とともに飽和磁化が低下する感温性がある鉄合金粒子をシリカ被覆してガリウムに分散させやすくして使用した。ガリウム中に3%程度の本粒子径の鉄合金粒子を分散させると、流体は外力でやわらかく変形するゲル状になった。本流体は流動性が少ないため、流動性がある磁性流体よりは懸濁液であるMR流体に近いと考えられる。この金属流体へ磁界の印加の有無によるトルクと角速度の関係を円錐平板型粘度計および共軸二重円筒型にて測定した。磁界中での流体の粘度変化が少なければ、応用として磁界の印加でオンとオフで移動できるスイッチ、あるいは、磁界印加状態で温度が変化すると流体が保持されなくなることによる温度スイッチなどが考えられる。