Huseyin Aydin Elhachmi Essadiqi In-Ho Jung Stephen Yue

出版者

一般社団法人 日本鉄鋼協会

雑誌

ISIJ International (ISSN:09151559)

巻号頁・発行日

vol.53, no.10, pp.1871-1880, 2013-10-15 (Released:2013-10-30)

参考文献数

22

被引用文献数

1 5

---

In the present work, the effects of intercritical annealing parameters on the microstructure and cold rollability (deformation rate and ratio) of “3rd Generation Advanced High Strength Steels (AHSS)” were studied. Hence, this paper discusses the formation of microstructures with different volume fractions of ferrite, martensite, bainite and retained austenite (RA). Two novel microstructures have been created, based on two levels of manganese (Mn): (i) ferrite plus martensite nucleated in austenite microstructure (FMNA structures), using Mn levels of 5 to 7 wt% and (ii) ferrite plus retained austenite duplex structure (FADP steels) for a Mn level of 10 wt%. In general, the ductility is a function of the amount of retained austenite and the strength is highly dependent on the martensite level.