著者

廣垣 和正 神谷 淳 木水 貢 山本 孝 田口 栄子 金法 順正 久田 研次 堀 照夫

出版者

社団法人 繊維学会

雑誌

繊維学会誌 (ISSN:00379875)

巻号頁・発行日

vol.66, no.4, pp.93-98, 2010 (Released:2010-06-01)

被引用文献数

1 1

---

Cyclodextrin (CD) was fixed onto a fabric using isocyanate as a cross-linker and their durability was discussed. The CDpolymer was insoluble on water, and reaction of CD with isocyanate was characterized with infrared spectroscopy. The poly(ethylene terephthalate) fabric was dipped into a solution of Beta-CD and isocyanate, and the fabric was annealed to fix CD. Weight decrease and CD content on the fabric was followed to evaluate the wash durability of the fabric. When CD was fixed with triisocyanate showed higher durability compared with the one fixed with diisocyanate. For the fabric with the highest durability, 60% of CD remained on the fabric even after 50 times washing. Absorption capacity of the CD on the fabric was evaluated to be 80% from the adsorption of phenolphthalein on a fabric

著者

堀 照夫 久田 研次

出版者

福井大学

雑誌

基盤研究(C)

巻号頁・発行日

2008

---

軽量で、高強度の導電性繊維およびプラスチックの製造を目的に、超臨界二酸化炭素流体の特徴を生かし、無電解めっきの核となる触媒の付与を検討した。超臨界二酸化炭素に比較的良く溶解する有機金属錯体の中から適切なものを数種選び、最初にこれらの錯体の単独での溶解性、2種類を混合した時の溶解性と相互作用について調べた。繊維・高分子としては高強度・高弾性で耐熱性の高いものを対象とした。アラミド繊維およびこのフィルムはジヘキサフロロアセチルアセテネートパラジウムなどを用い、錯体を注入した後、高温で乾熱処理することで高いめっき密着性が達成できた。液晶高分子であるLCPやエポキシについては密着性の向上に工夫を要した。解決法の一つは構造の類似な2種の錯体を混合使用する方法で、これにより超臨界流体に対する溶解性が向上し、めっき触媒であるパラジウムを強固に高分子表面に固定できた。その他に高分子表面を電子線加工する方法、プラズマ処理する方法、レーザー照射する方法等も効果があることを明らかにした。