The present paper is a brief review of our recent works on the crystal structures, structural disorders and ion-diffusion paths of various ionic and mixed conductors. Diffusion paths along the <100> directions are observed in the fluorite-type ionic conductors such as δ-Bi1.4Yb0.6O3, Ce0.93Y0.07O1.96, Y0.785Ta0.215O1.715 and α-CuI. In the prerovskite-type and double-prerovskite-type conductors, the mobile oxide ions move along the <100> directions near the stable positions and along <110> around the midway of diffusion pathway. The cubic prerovskite-type and double-prerovskite-type conductors exhibit three- and two-dimensional networks of diffusion pathways, respectively. K2NiF4-type conductor has a two-dimensional network of diffusion pathway through interstitial oxide ions. The oxide ions in apatite-type conductors diffuse along the hexagonal c-axis. The diffusion paths of two lithium-ion conductors are also presented.

著者

八島 正知 石原 達己 藤井 孝太郎

出版者

東京工業大学

雑誌

基盤研究(A)

巻号頁・発行日

2012-04-01

---

我々の研究プロジェクト「d10金属酸化物新イオン伝導体の構造デザイン」の概要を記す。Pr2(Ni,Cu,Ga)O4イオン伝導性材料ではNi2.5+に比べて高い価数を持つGa3+を添加することで格子間酸素量(キャリア濃度)が増加して酸素透過率が向上すること見いだされた。新物質探索の結果、新しい構造ファミリーNdBaInO4を発見した。SrをNdBaInO4に添加すると酸化物イオン伝導度が向上することも見出した。Pr2(Ni,Cu,Ga)O4, PrBaCo2O5.5+delta, Ce0.5Zr0.5O2の酸化物イオンの拡散経路を研究した。K2NiF4型A2BO4酸化物の異方性熱膨張を研究した。