Effects of mold temperature and injection pressure on mechanical properties and surface defects of Na2CO3-20mol%NaCl-30mol%KCl salt-mixtures made by high pressure die-casting machine were investigated. The bending strength of the salt-mixture was increased with increasing mold temperature, while the injection pressure in the temperature range from 39MPa to 78MPa was not influenced by the bending strength. Results of the Weibull statistics analysis suggest that increasing the mold temperature is effective for increasing the reliability of the strength as well as the bending strength, because the surface crack decreases with increasing mold temperature. In addition, we succeeded in making a salt core for single closed deck type cylinder blocks. These results suggest that the Na2C03-NaCl-KCl salt-mixtures made by die-casting machine are promising core material for aluminum alloy high pressure die-castings.