1 0 0 0 OA ダイカストマシンで成形した混合塩中子の機械的性質
- 著者
- 及川 勝成 目黒 賢一 八百川 盾 安斎 浩一 山田 養司 藤原 彰人 吉井 大
- 出版者
- 公益社団法人 日本鋳造工学会
- 雑誌
- 鋳造工学 (ISSN:13420429)
- 巻号頁・発行日
- vol.81, no.5, pp.232-237, 2009-05-25 (Released:2014-08-12)
- 参考文献数
- 14
- 被引用文献数
- 1
Effects of mold temperature and injection pressure on mechanical properties and surface defects of Na2CO3-20mol%NaCl-30mol%KCl salt-mixtures made by high pressure die-casting machine were investigated. The bending strength of the salt-mixture was increased with increasing mold temperature, while the injection pressure in the temperature range from 39MPa to 78MPa was not influenced by the bending strength. Results of the Weibull statistics analysis suggest that increasing the mold temperature is effective for increasing the reliability of the strength as well as the bending strength, because the surface crack decreases with increasing mold temperature. In addition, we succeeded in making a salt core for single closed deck type cylinder blocks. These results suggest that the Na2C03-NaCl-KCl salt-mixtures made by die-casting machine are promising core material for aluminum alloy high pressure die-castings.
1 0 0 0 OA 新機能Co基合金-その相安定性と工業材料への展開
Co基合金の状態図について実験ならびにCalphad法による熱力学解析を行い、Co基熱力学・状態図データベースを世界に先駆けて構築した。このデータベースを基に新しいL1_2化合物γ' 相Co_3(Al, W)を利用したCo基スーパーアロイの合金設計を行い、800℃で10万時間のクリープ推定強度が100MPa以上を期待できる鍛造用合金を開発し、また鋳造合金の応用としてFSW(摩擦撹拌接合)用ツールに適用し、商品化に成功した。また磁性材料としてCo基磁気材料としてCo-W基合金薄膜とCo基ホイスラー合金が磁気記録材およびスピントロニクスとして有望である事を示した。さらに生体材料としてCo-Al基合金のγ (fcc)/β (B2)層状組織を利用したポーラス化を行ない、そのための最適組成、熱処理条件を明らかにした。