1 0 0 0 OA SiC繊維のアルミニウムマトリックスに対する適合性
- 著者
- 小原 嗣朗 武藤 範雄
- 出版者
- 公益社団法人 日本金属学会
- 雑誌
- 日本金属学会誌 (ISSN:00214876)
- 巻号頁・発行日
- vol.45, no.4, pp.411-416, 1981 (Released:2008-04-04)
- 参考文献数
- 17
- 被引用文献数
- 12 9
The compatibility of SiC fibers with aluminum was investigated. The SiC fibers made from an organosilicon polymer was used in the present study. The fiber specimens were aluminum-coated by vacuum evaporation and heat treated at temperatures 673 to 873 K for 90 ks, or 973 to 1373 K for 1.8 ks in an argon atmosphere. Then, the fiber specimens were tensile tested at room temperature.For the solid state aluminum, the SiC fibers showed no loss in tensile strength after the heat treatments at 673 to 773 K, but showed a slight degradation in tensile strength after the heat treatment at 873 K. For the liquid state aluminum, the SiC fibers showed a noticeable degradation in tensile strength after the heat treatments at temperatures higher than 973 K. However, the degradation in tensile strength was decreased in the solid and the liquid state by alloying Si with aluminum.
1 0 0 0 OA グラファイト-FRP積層材ノズルの研究(<特集>観測ロケット基礎開発研究特集号)
- 著者
- 小原 嗣朗 武藤 範雄 KOHARA Shiro MUTO Norio
- 出版者
- 東京大学宇宙航空研究所
- 雑誌
- 東京大学宇宙航空研究所報告 (ISSN:05638100)
- 巻号頁・発行日
- vol.13, no.1_B, pp.379-402, 1977-03
グラファイトノズルとFRPノズルの長所を合わせた性質をもつノズルとして,グラファイト-FRP積層材ノズルの研究を進めた。グラファイトおよびFRPの性質に関する基礎的な研究を行った後,小型の積層材ノズルを作り,テストスタンドで燃焼実験を行った。各種の推薬を用い,種々な条件における燃焼実験を繰返して,実用に供し得る程度の性能をもつ積層材ノズルを開発した。