Mn-modified hexagonal YbFeO3 (Mn-YFO) synthesized by a solvothemal method is found to have a higher catalytic activity for C3H8 or CO oxidation than noble metal catalyst, Pd/Al2O3. The catalytic activity is mainly due to amorphous MnOx species located on ab plane of the hexagonal lattice. A small amount of Pd loading on Mn-YFO drastically enhances the catalytic activity; that is, 0.5 wt% Pd/Mn-YFO shows excellent activity for CO oxidation that exceeds the activity of 2.0 wt% Pd/Al2O3. The Pd loading dramatically improves the reducibility of the MnOx species and also CO adsorption to Mn-YFO. Thus, we demonstrate that an extremely small amount of Pd species plays a role as a promoter for the catalytic and reduction functions of the MnOx species on Mn-YFO. It is expected that the establishment of such promoter effect will provide a novel guideline for reducing the use of precious metal resources.

著者

細川 三郎

出版者

京都大学

雑誌

若手研究(A)

巻号頁・発行日

2011-04-01

---

六方晶構造を有する希土類―鉄複合酸化物(h-REFeO3)は準安定相構造であるが故に,常法では合成が困難である.本研究では,共沈法および錯体重合法で得られた前駆体の結晶化過程を詳細に検討することで,h-REFeO3の効率的・選択的な合成を試みた.その結果,焼成時間を調整することで単相のh-REFeO3が得られることを見出した.飛躍的に高いC3H8燃焼活性を有する触媒開発を目指し,異種遷移金属で修飾したh-YbFeO3のソルボサーマル合成を検討した.Mn修飾h-YbFeO3は他の遷移金属を修飾したものより極めて高い活性を示し,貴金属触媒であるPd/Al2O3よりも高い活性を示すことを見出した.