2 0 0 0 OA 多孔性無機膜によるナノ濾過
- 著者
- 都留 稔了
- 出版者
- 日本膜学会
- 雑誌
- 膜 (ISSN:03851036)
- 巻号頁・発行日
- vol.23, no.2, pp.70-79, 1998-03-01 (Released:2011-03-04)
- 参考文献数
- 56
Nanofiltration by porous inorganic membranes is reviewed from the viewpoint of preparation methods as well as the applications. Sol-gel methods have been widely applied to fabricate porous inorganic membranes, and alumina, titania, zirconia and silica-zirconia have been successfully applied to fabricate inorganic membranes having nanofiltration performance.Summarized are also other preparation techniques including pyrolysis of polymeric membranes, organic/inorganic hybrid membranes, hydrothermal method for zeolite membranes, anodic oxidation, dynamic membranes, clay membranes. Applications of inorganic membranes reviewed are categorized into separation of electrolytes, nanofiltration of organic solutions, electro-ultrafiltration and membrane reactor application.
1 0 0 0 多孔性シリカ膜におけるアンモニア透過特性
- 著者
- 金指 正言 山本 章 吉岡 朋久 都留 稔了
- 出版者
- 公益社団法人 化学工学会
- 雑誌
- 化学工学会 研究発表講演要旨集
- 巻号頁・発行日
- vol.2009, pp.189, 2009
1 0 0 0 OA 多孔性シリカ膜におけるアンモニア透過特性
- 著者
- 金指 正言 山本 章 吉岡 朋久 都留 稔了
- 出版者
- 公益社団法人 化学工学会
- 雑誌
- 化学工学会 研究発表講演要旨集 化学工学会第74年会
- 巻号頁・発行日
- pp.189, 2009 (Released:2009-09-16)
1 0 0 0 OA セラミック逆浸透膜の創製とマイクロポア透過特性
橋かけアルコキシドとしてビス(トリエトキシリシリル)エタン(BTESE)を用いて,有機無機ハイブリッド逆浸透膜の開発を行ない,その透過特性の評価を行った。BTESE 膜は 95%以上の脱塩率を示し,逆浸透膜として可能性を明らかとした。90℃でも安定な濾過性能を示しただけでなく,塩素に対しても良好な耐性を示した。さらに,透過機構について,供給溶液濃度,操作圧力,温度依存性を検討した。操作圧力の増加とともに,透過流束および阻止率が上昇したのに対して,塩濃度の増加とともに両者ともに低下した。一方,操作温度とともに阻止率および透過流束が向上したが,その温度依存性は水粘度の温度依存性よりも大きいことから,透過機構は粘性流れとは異なることを明らかとした。