著者

佐野 真弘 柴山 充弘 櫻井 伸一 黒川 秀信 野村 春治

出版者

The Society of Fiber Science and Technology, Japan

雑誌

繊維学会誌 (ISSN:00379875)

巻号頁・発行日

vol.48, no.2, pp.74-83, 1992-02-10 (Released:2008-11-28)

参考文献数

32

被引用文献数

1 1

---

Poly (vinyl alcohol) (PVA) reacts with borate ions to give a thermoreversible gel. In this work, gel films (PVA-G) were successfully prepared by drying this gel or by soaking PVA films (PVA-O; crosslink-free PVA films) in a solution containing borate ions. On the other hand, the crosslinks formed in PVA-G can be removed by soaking PVA-G in an acid solution. The mechanical properties and structure of PVA-G were investigated by means of dynamic viscoelastic, wide angle X-ray diffraction, hot water resistance and thermogravimetric measurements, and were compared with those of PVA-O.The results of dynamic viscoelastic measurements show that PVA-G retains a high value in storage modulus up to ca. 200°C which are different from PVA-O. In addition, there appeared a mechanical dispersion around ca. 220°C. Wide angle X-ray diffraction patterns show that the crystallite size of PVA-G is smaller than PVA-O. The characteristic behaviors in viscoelasticity are explained by the presence of crosslinks and/or crystallite size. Hot water resistance of PVA-G was also found to be improved by the introduction of crosslinks.

著者

羽田 次夫 清瀬 篤信 高橋 重三 野村 春治 黒川 正隆

出版者

The Society of Polymer Science, Japan

雑誌

高分子論文集 (ISSN:03862186)

巻号頁・発行日

vol.40, no.6, pp.383-391, 1983

被引用文献数

1 3

---

ポリテトラフルオロエチレン (PTFE) の構造を明らかにするため, ディスパーション粒子を圧縮, 圧延して作った生テープの構造を熱分析 (示差熱分析, 熱機械分析), X線回折, 電子顕微鏡で調べた. 生テープはディスパーション粒子が圧着しており, X線回折図は配向を示す. 焼結時にほぼ無配向となり, 冷却により再びめいりょうな配向構造にもどる. 冷却速度を遅くすると, 圧延方向に平行な縞 (Striation) を持つバンド構造が割断面に現れる. 焼結時間が長くなると配向構造から無配向構造へと変化する. 熱機械測定によって, PTFE生テープは溶融状態においてさえ, 焼結前の履歴を長く保っていることが明らかになった. 十分に履歴を解消するには約450℃の高温または低温で長時間, 例えば370℃で2時間以上の焼結が生テープでは必要である.