Purpose: This study evaluated the influence of firing procedures and layering thickness of porcelain on internal adaptation of maxillary anterior cantilever zirconia resin-bonded fixed dental prostheses (RBFDPs). Methods: The maxillary right central incisor on a model was prepared for a single-retainer zirconia RBFDP. A total of 36 frameworks of cantilever zirconia RBFDPs were classified into three groups (CB0.5, CB1.0, and CB2.0 groups) based on the thickness of the cut-back on the facial surface (0.5 mm, 1.0 mm, and 2.0 mm, respectively). Feldspathic porcelain was layered onto the facial surface of the zirconia RBFDP frameworks. Internal space widths between the abutment tooth and the framework were measured before and after porcelain firing by a replica technique. The internal space values before and after porcelain firings were compared using the paired t-test within the same group (α = 0.05). Differences in internal space values (distortion) between before and after porcelain firing were compared using one-way analysis of varianc e and Tukey multiple comparison tests. Results: For all framework designs, internal space values after porcelain firing were significantly higher than those before firing. Among all groups, the CB0.5 group showed the lowest internal distortion values for the whole measured area. The CB2.0 group showed higher distortion values than the CB1.0 group. Conclusions: Porcelain firing procedures negatively impacted the internal space in cantilever zirconia RBFDPs. In addition, the increased volume of layering porcelain had a negative effect on the internal distortion of ma xillary anterior cantilever zirconia RBFDPs.

著者

Futoshi Komine Junichi Honda Kosuke Kusaba Kei Kubochi Hiroki Takata Masanori Fujisawa

出版者

Nihon University School of Dentistry

雑誌

Journal of Oral Science (ISSN:13434934)

巻号頁・発行日

pp.20-0195, (Released:2020-08-01)

参考文献数

20

被引用文献数

5

---

Computer-aided design/computer-aided manufacturing (CAD/CAM) restorative materials have been widely used owing to a number of advantages, including stable quality of the materials, lower costs, and time-saving factors. Resin-based CAD/CAM materials for definitive restorations are classified into two groups: dispersed nanoparticle-filled composite resin and polymer-infiltrated-ceramic-network materials. Resin-based CAD/CAM materials have been applied to single crown restorations as a monolithic structure for the posterior region. In addition, resin-based CAD/CAM restorations have been applied recently for the anterior area. This literature review summarizes clinical outcomes, such as survival rates and clinical complications of single crown restorations fabricated with resin-based CAD/CAM materials.

著者

Yuta MORIYA Futoshi KOMINE Junichi HONDA Kosuke KUSABA Jin KITANI Hideo MATSUMURA

出版者

The Japanese Society for Dental Materials and Devices

雑誌

Dental Materials Journal (ISSN:02874547)

巻号頁・発行日

pp.2019-216, (Released:2020-05-22)

参考文献数

29

---

To investigate the effect of luting agent type on fracture loads of implant-supported ceramic prostheses in premolar region. Ninety-nine implant-abutment complexes were divided into three different implant-supported prostheses: monolithic yttria-partially stabilized zirconia (Y-PSZ) restorations (MPZ specimens), porcelain layered on yttria-stabilized tetragonal zirconia polycrystal (Y-TZP) restorations (PLZ specimens), and monolithic lithium disilicate ceramic restorations (MLD specimens). Implant-supported prostheses were luted with adhesive resin luting agent (RLA), glass ionomer cement (GIC), or zinc phosphate cement (ZPC). For MPZ and MLD specimens, fracture loads were significantly higher for RLA group than for GIC and ZPC groups. For PLZ specimens, fracture loads did not significantly differ in relation to luting agent. Fracture loads were significantly higher for MPZ specimens than for other test specimens, regardless of luting agent. Use of an adhesive resin luting agent is recommended for placement of premolar implant-supported monolithic Y-PSZ and lithium disilicate ceramic prostheses.

著者

Ryosuke FUSHIKI Futoshi KOMINE Fumiaki KIMURA Kosuke KUSABA Tomohide KONDO Yuta MORIYA Hideo MATSUMURA

出版者

The Japanese Society for Dental Materials and Devices

雑誌

Dental Materials Journal (ISSN:02874547)

巻号頁・発行日

pp.2018-253, (Released:2019-05-17)

参考文献数

34

被引用文献数

3

---

This study evaluated shear bond strengths of two gingiva-colored layering resin composites to zirconia frameworks coated with feldspathic porcelain. Airborne-particle abraded porcelain-coated zirconia disks were treated with one of the following primers: Clearfil Photo Bond, Clearfil Photo Bond with Clearfil Porcelain Bond Activator (CPB+Activator), Estenia Opaque Primer, Porcelain Liner M Liquid B (PLB), or no primer. A light-polymerizing (CER) or a photo/heat-polymerizing gingiva-colored indirect resin composite (EST) was bonded to the porcelain-coated zirconia disks in each group (n=11). Shear bond strength was measured. For both CER and EST specimens, bond strengths in CPB+Act group were significantly higher than those in the other groups. In all priming groups, bond strength was significantly higher for EST specimens than for CER specimens. Combined application of a phosphate monomer and silane enhanced initial bond strength of light-polymerized and photo/heat-polymerized gingiva-colored layering resin composites to porcelain-coated zirconia ceramics.