This study investigated the effect of 10-methacryloyloxydecyl dihydrogen phosphate (MDP) in methyl methacrylate (MMA) monomer on the adhesion of tri-n-butylborane (TBB)-initiated resins (MDP/MMA-TBB resins) to human enamel. Enamel surface conditions were either polished only or phosphatized surfaces. The 1.0, 1.7, and 2.0 mol% MDP/MMA-TBB resins, 4-methacryloxyethyl trimellitate anhydride (4-META)/MMA-TBB resin and MMA-TBB resin were prepared as luting materials. The shear bond strength was determined before and after thermocycles, and the results were compared using non-parametric statistical analyses (each, n=15). The MDP/MMA-TBB resins showed significantly better bond durability to enamel than other resins with or without etching. The 1.7 and 2.0 mol% MDP/MMA-TBB resins were suggested to be the optimum MDP concentrations from pre- and post-thermocycling results for the non-etched specimens. The TBB initiator resin including MDP was shown to be effective in bonding to human enamel, and this effect was enhanced in combination with phosphate treatment.
著者
Haruto Hiraba Hiroyasu Koizumi Akihisa Kodaira Kosuke Takehana Takayuki Yoneyama Hideo Matsumura
出版者
Japan Prosthodontic Society
雑誌
Journal of Prosthodontic Research (ISSN:18831958)
巻号頁・発行日
pp.JPR_D_21_00308, (Released:2022-05-14)
参考文献数
32
被引用文献数
1

Purpose: To clarify the effect of a multi-purpose primer combining several functional monomers on two prosthodontic materials (cast titanium and a gold alloy) after airborne-particle abrasion.Methods: Disk-shaped adherends were prepared from cast titanium (CP Titanium JIS2) and a gold alloy (Casting Gold M.C. Type IV). A silane-containing two-liquid primer (M&C primer (MC)) and two silane-free single-liquid primers (Alloy Primer (AP) and V-Primer (VP)) were used as surface-treatment agents. The shear bond strengths were determined before and after thermocycling to evaluate the adhesive durability, and the results were compared using a non-parametric statistical analysis. The effect of airborne-particle abrasion with alumina on the titanium surface was analyzed by X-ray photoelectron spectroscopy (XPS).Results: There was no significant difference in bond strength between the MC and AP before and after thermocycling, whereas VP showed significantly lower values. XPS revealed that the titanium acquired hydrophilic properties after the airborne-particle abrasion.Conclusions: The novelty of this study is that it shows that the presence/absence of the silane had no effect on the bonding of cast titanium with an acrylic resin. The study also showed that the multi-purpose primer can be used without any problems with both cast titanium and gold alloy, in combination with airborne-particle abrasion with alumina.
著者
Kosuke TAKEHANA Hiroyasu KOIZUMI Haruto HIRABA Akihisa KODAIRA Takayuki YONEYAMA Hideo MATSUMURA
出版者
The Japanese Society for Dental Materials and Devices
雑誌
Dental Materials Journal (ISSN:02874547)
巻号頁・発行日
pp.2021-181, (Released:2021-12-28)
参考文献数
23

This study assessed the effect of a primer containing 10-methacryloyloxydecyl-(2-thiohydantoin-4-yl)propionate (MDTHP) on the bonding of noble metal alloys to an acrylic resin. Three noble metal alloys were selected as adherends, and V-Primer containing 6-(4-vinylbenzyl-n-propyl)amino-1,3,5-triazine-2,4-dithione was used as a comparative control. The disk specimens of each noble metal alloy were wet-ground and divided into three conditions: specimens primed with MDTHP primer or V-Primer, and specimens without priming. An acrylic resin was bonded to each specimen, and the specimens were performed the shear bond test. The MDTHP primer showed higher shear bond strength than the V-Primer for all specimens. X-ray photoelectron spectroscopic analysis showed that MDTHP was adsorbed on the Au-Pt-Pd alloy surface even after acetone cleaning. MDTHP binds not only with Cu but also with Au and Ag, promoting the bond strength of noble metal alloys. The effectiveness of MDTHP on dental noble metal alloys was suggested.