- Futoshi KOMINE Shingo KAMIO Hiroki TAKATA Shogo YAGAWA Serina TAGUCHI Kohei TAGUCHI Akiko HASHIGUCHI Hideo MATSUMURA
- 出版者
- 日本歯科理工学会
- 雑誌
- Dental Materials Journal (ISSN:02874547)
- 巻号頁・発行日
- pp.2017-057, (Released:2017-09-07)
- 参考文献数
- 41
- 被引用文献数
- 3
This study evaluated the effect of zirconia framework design on fracture load of implant-supported zirconia-based prostheses after thermal cycling and mechanical loading. Three different zirconia framework designs were investigated: uniform-thickness (UNI), anatomic (ANA), and supported anatomic (SUP) designs. Each framework was layered with feldspathic porcelain (ZAC group) or indirect composite material (ZIC group). The specimens then underwent fracture load testing after thermal cycling and cyclic loading. In the ZAC group, mean fracture load was significantly lower for UNI design specimens than for the other framework designs. In the ZIC group, there was no significant difference in mean fracture load between ANA design specimens and either UNI or SUP design specimens. To improve fracture resistance of implant-supported zirconia-based prostheses after artificial aging, uniformly thick layering material and appropriate lingual support with zirconia frameworks should be provided.
- 著者
- Futoshi KOMINE Kohei TAGUCHI Ryosuke FUSHIKI Shingo KAMIO Taro IWASAKI Hideo MATSUMURA
- 出版者
- 日本歯科理工学会
- 雑誌
- Dental Materials Journal (ISSN:02874547)
- 巻号頁・発行日
- vol.33, no.5, pp.607-613, 2014-09-30 (Released:2014-10-01)
- 参考文献数
- 29
- 被引用文献数
- 1 16
This study evaluated fracture load of single-tooth, implant-supported, zirconia-based, porcelain- and indirect composite-layered restorations after artificial aging. Forty-four zirconia-based molar restorations were fabricated on implant abutments and divided into four groups, namely, zirconia-based all-ceramic restorations (ZAC group) and three types of zirconia-based composite-layered restorations (ZIC-P, ZIC-E, and ZIC groups). Before layering an indirect composite material, the zirconia copings in the ZIC-P and ZIC-E groups were primed with Clearfil Photo Bond and Estenia Opaque Primer, respectively. All restorations were cemented on the abutments with glass-ionomer cement and then subjected to thermal cycling and cyclic loading. All specimens survived thermal cycling and cyclic loading. The fracture load of the ZIC-P group (2.72 kN) was not significantly different from that of the ZAC group (3.05 kN). The fracture load of the zirconia-based composite-layered restoration primed with Clearfil Photo Bond (ZIC-P) was comparable to that of the zirconia-based all-ceramic restoration (ZAC) after artificial aging.