著者
李 世欽 鈴木 清 中川 威雄
出版者
一般社団法人 粉体粉末冶金協会
雑誌
粉体および粉末冶金 (ISSN:05328799)
巻号頁・発行日
vol.35, no.6, pp.552-557, 1988

For further development of the high performance self-lubrication materials being proof against vacuum or high temperature, cast iron fibre composites containing a large amount of graphite were investigated. The cast iron fibre of 20-40 μm in diameter and 1.2 mm in length, which was prepared by chatter-machining a ductile cast iron bar, was mixed with graphite powder and consolidated by compacting in a die, sintering and finally repressing. The optimum conditions for the processing were determined experimentally, and the composite of the almost same mechanical strength as grey iron was made with an addition of 28.8 vol% graphite. In conclusion the fibre metallurgical processing of the high performance self-lubrication composite materials of cast iron and graphite is feasible in the production.
著者
中川 威雄 鈴木 清 植松 哲太郎 小山 浩幸
出版者
公益社団法人精密工学会
雑誌
精密機械 (ISSN:03743543)
巻号頁・発行日
vol.47, no.11, pp.1399-1405, 1981-11-05
被引用文献数
10

金属短繊維は, 複合材料用基材など種々の用途をもつものと考えられているが, 既存の金属短繊維製造法はいずれも効率が悪く, コストも高い.本論文では, 旋削時に弾性切削工具にびびり振動を積極的に生じさせることにより極細の金属短繊維を製造する, 新しい「びびり振動切削法」を提案する.このびびり振動切削法によれば, 直径10〜250μm, 長さ0.5〜20mmの金属短繊維を, ほとんどすべての金属材料から直接, 安価に, 効率良く製造できる.びびり振動切削法における短繊維の生成機構についても実験により得られた結果をもとにその推定を行った.