Reduction melting methods to remove Pb from lead silicate glasses such as cathode ray tube funnel glass have been extensively studied. In this paper, reduction melting of a model lead glass was conducted using printed circuit board as reductant. Model lead silicate glass, viscosity reducing agent (Na2CO3), and printed circuit board were mixed and melted at 1473 K. Metal phase mainly composed of Pb was formed and settled in the melting glass residue. With increasing printed circuit board addition, the amount of metal phase increased and the concentrations of PbO remained in the glass residue decreased, indicating that addition of printed circuit board is effective to remove Pb from the Pb glass. By EDS analysis, it was confirmed that Cu, Ni and Sn are contained in the metal phase, indicating that metals in printed circuit board are recovered with Pb.

著者

高橋 徹 富田 恵一 若杉 郷臣 山田 敦 折橋 健 古賀 信也

出版者

一般社団法人 廃棄物資源循環学会

雑誌

廃棄物学会研究発表会講演論文集 第19回廃棄物学会研究発表会

巻号頁・発行日

pp.208, 2008 (Released:2008-11-25)

被引用文献数

1

---

木質系バイオマス燃焼灰の化学組成および有害物質の溶出試験について検討した結果、燃焼灰には肥料主成分が多く含まれており、肥料として十分に利用できることが分かった。また一部の木質バイオマス燃焼灰の溶出液には基準値以上の六価クロム溶出が確認されており、ストーブ材質からの腐食、防腐剤を原料とした燃料からの汚染および木質ペレット燃料中に含有していると推測される。ペレット原料中のクロムは自然由来ではなく,破砕工程,おが粉製造工程およびペレット製造工程で混入したクロムが燃焼し,濃縮・酸化され,六価クロムの溶出が発生したと考えられる。さらに、木質バイオマス燃焼灰を有効利用するために、堆肥と燃焼灰を混合したペレットを製造し、肥料としての安全性を検討した結果、有害成分は基準値以下であり、有害金属溶出試験についても全ての項目で基準値以下であった。混合ペレットは肥料として安全に使用できることが分かった。