著者

曾 敏 上川 直文 小島 隆 掛川 一幸

出版者

公益社団法人日本セラミックス協会

雑誌

日本セラミックス協会学術論文誌 : Nippon Seramikkusu Kyokai gakujutsu ronbunshi = Journal of the Ceramic Society of Japan (ISSN:13486535)

巻号頁・発行日

vol.115, no.1348, pp.840-845, 2007-12-01

被引用文献数

5

---

The titania particles were prepared by aging the mixture of titanium isopropoxide (TIP) and H_2O at 318 K. The anatase titania particles were obtained by the aging procedure at 318 K for more than 16 h. The aging temperature was quite low to obtain anatase-type titania particles. According to the DTA measurement, the amount of amorphous phase included in the titania particles decreased with increases in the aging time. Furthermore, the titania particles obtained by aging the mixture of TIP and H_2O at 318 K for 24 h contained no amorphous phase. The obtained titania particles had a high BET specific surface area of more than 250m^2/g. To characterize the titania surface, the adsorption isotherms of the organic dye molecules in an aqueous solution were measured. The negatively charged Evans blue molecules strongly adsorbed on the titania surface obtained by the low-temperature hydrolysis reaction as compared with the results of the methylene blue molecules. Furthermore, the decomposition kinetics of the dye molecules by the photocatalytic activity also deepened with the charge of the dye molecules. The relation between the UV irradiation time and the molar ratio of the decomposed dye molecules followed the Avrami equation. According to the results of the analysis using the Avrami equation, the Evans blue molecules were decomposed on the titania particle surface. In contrast, the methylene blue molecules were decomposed in the aqueous solution. The difference in kinetics was related to the interaction of the dye molecules and the titania surface. The high surface area of the titania particles obtained the low-temperature hydrolysis reaction of titanium alkoxides enhanced the effect of the surface interaction on kinetics of the photocatalytic activity.

著者

鈴木 弘孝 小島 隆矢 嶋田 俊平 野島 義照 田代 順孝

出版者

日本緑化工学会

雑誌

日本緑化工学会誌 (ISSN:09167439)

巻号頁・発行日

vol.31, no.2, pp.247-259, 2005-11-30

被引用文献数

7 9

---

本研究は, 近年ヒートアイランド対策や地球温暖化防止対策への対応等環境負荷の少ない都市環境を形成していくための有力な手法として着目されている壁面緑化について, 現在屋上の緑化や開発利用に取り組んでいる企業とその技術担当者へのアンケート調査結果に基づき, 壁面緑化の市場性, 普及の可能性等について民間企業と技術担当者の意識を把握し, 技術的課題への認識を整理することにより, 今後都市部において壁面緑化を推進していく上での技術開発の方向, 研究開発分野において重点的に取り組むべき対象と範囲を検討するための基礎的資料を得ることを目的としている。調査の結果, 民間企業等の意識として壁面緑化の今後の市場性拡大への期待が高いこと, 技術担当者の意識として壁面緑化に関する技術開発を推進していく上で, 緑化による温熱環境改善効果の定量化, 建設コストの縮減, 維持管理の簡素・効率化等を課題と認識していること, また壁面緑化の6種類のタイプについて対応分析を行った結果, 適用場所や普及可能性に認識の差異のあることが明らかとなった。