著者

田辺 実 常盤 匡 小泉 忠由

出版者

The Japan Society of Mechanical Engineers

雑誌

日本機械学会論文集 (ISSN:21879761)

巻号頁・発行日

vol.80, no.817, pp.DSM0274-DSM0274, 2014

---

The relationship between the elements included in materials and the fire ball obtained by spark test, that is simple, has been examined by using SEM photographing of the fire ball. From experimental results, the kind of steel material could be estimated from fireballs image of SEM. The following contents would be pointed out as the results. The size of fire ball becomes large with the increase in the contained carbon. The size of alloy steels becomes about the double of fire ball of carbon steel. When nickel element is contained in a material, the surface of fire ball shows the delamination. When the many chromium components are contained the size of fire ball becomes large, and many holes occur in the fireball. The presence of molybdenum element in the steel shows the smooth texture at the surface of the fireball. The wrinkles appear at the surface of the fireball by the presence of tungsten element, and the many holes occur in the fireball. Whether the material is ductile or brittle we would be estimated from the pattern of deformation of the hole of the fire ball. The kind of material would be able to distinguish from the qualitative properties of the fire ball.

著者

小泉 忠由 伊東 誼 益子 正巳

出版者

公益社団法人精密工学会

雑誌

精密機械 (ISSN:03743543)

巻号頁・発行日

vol.46, no.3, pp.338-343, 1980-03-05

被引用文献数

1

---

本研究はボルト結合部の正負方向に繰返し接線方向荷重を作用させ結合面の接線方向変位を減衰能と密接に関係するヒステリシスループに重点をおき実験的に検討している。実験結果によるとヒステリシスループの面積は振幅のn乗に比例し、nは1.8〜2.8くらいの値を示す。このnの値から結合面の減衰特性が振幅依存性を示す指数関数的な減衰振幅を示すことが説明できる。また、接線方向荷重速度を変えることにより微小すべり域の速度特性を検討し、荷重速度の増大とともに微小すべりも増大し、ヒステリシスループの面積が大きくなることを確認し、予すべり域においても従来の摩擦特性と同じ挙動を示すことを確かめている。また、ヒステリシスループの挙動から結合面の減衰特性を検討し、かつボルト結合部の減衰能を等価粘性減衰定数の値として求め、ヒステリシスループを用いることにより、ボルト結合部の減衰能をある程度推定することができることを示している。