著者

稲葉 信幸 宮島 英紀 武富 荒 近角 聡信

出版者

公益社団法人 日本磁気学会

雑誌

日本応用磁気学会誌 (ISSN:02850192)

巻号頁・発行日

vol.13, no.2, pp.245-248, 1989-04-30 (Released:2007-12-07)

参考文献数

4

被引用文献数

2 2

---

Magnetization (M), field induced magnetic anisotropy (Ku), rotational hysteresis loss (Erot) and melting point (Tm)f water- and paraffin-base ferrofluids were investigated in a temperature range from 77 K to 300 K as a function of the density of colloidal particles. Both paraffin and paraffin-base fluids were melted down at the temperature range from 180 to 210 K. In this range, the values of M and Erot, for paraffin-base fluids increased and Ku decreased with increasing temperature. These properties are interpreted by assuming that liquid-state and solid-state parts in paraffin exist in this tempetarure range and that the volume of solid-state part decreases with increasing temperature. The freezing point depression was observed in water-base fluids.

著者

稲葉 信幸 宮島 英紀 武富 荒 近角 聡信

出版者

公益社団法人 日本磁気学会

雑誌

日本応用磁気学会誌 (ISSN:02850192)

巻号頁・発行日

vol.12, no.2, pp.283-286, 1988-04-30 (Released:2007-12-07)

参考文献数

6

被引用文献数

5 3

---

The magnetization process of a ferrofluid whose carrier fluid is paraffin was investigated in a temperature range from 77K to 300K as a function of the intensity of cooling field and the freezing rate. Phase transition between liquid state and solid state can be simulated by using the ferrofluids as a magnetic probe. The uniaxial magnetic anisotropy was induced by field cooling in frozen ferrofluids. This induced anisotropy decreased with increasing temperature near the melting point and disappeared at 30K higher temperature than the melting point. In this region the rotational hysteresis was observed. The anisotropy constant K near the melting point was described by the equation K=A·exp(ΔEK/kT). The value of the activation energy ΔEK was almost the same as that of ΔEη estimated from the viscosity vs. temperature relation η∝ exp(ΔEη/kT).

著者

二本 正昭 稲葉 信幸 平山 義幸 木本 浩司 宇佐美 勝久

出版者

一般社団法人電子情報通信学会

雑誌

電子情報通信学会技術研究報告. MR, 磁気記録

巻号頁・発行日

vol.95, no.383, pp.35-42, 1995-11-23

被引用文献数

3

---

CoCrTa薄膜媒体の組成的微細構造を解明することを目的に、分析機能を持つ高分解能電子顕微鏡法により、面内および垂直磁気記録媒体として検討されているCoCrTa媒体の微細構造を調べた。高い基板温度で形成した媒体では、面内および垂直磁気記録媒体のいずれの媒体でも、結晶粒界に25at.%を超えるCrの強い偏析層が観察された。このCrに富んだ偏析層の厚さは、1.5〜2nmと解釈された。CoCrTa面内媒体のバイクリスタル結晶粒界のCr偏析量は通常の結晶粒界の組成に比べ、若干低い値が得られた。結晶粒内のCr量は膜の平均組成より低く、しかも6〜12%程度の範囲で揺らいで分布していることが分かった。膜の形成基板温度、磁気特性および組成偏析構造の関係を調べた結果、Cr偏析構造と保磁力には密接な関係があることが確認された。