This study examined the effect of silane and phosphate functional monomer on bond strengths between a resin-based luting agent joined to a lithium disilicate ceramic (IPS e.max) and silica (quartz) materials. The e.max and quartz specimens were assigned to 6 groups with different priming/bonding agents, namely, Clearfil Porcelain Bond Activator, Clearfil Photo Bond, Clearfil Photo Bond Universal with Clearfil Porcelain Bond Activator, Clearfil Photo Bond Catalyst with Clearfil Porcelain Bond Activator, Clearfil Photo Bond with Clearfil Porcelain Bond Activator, and unprimed. The corresponding specimens were bonded by using a resin-based luting agent (Panavia V5). Shear bond strengths were determined before and after 5,000 thermocycles. For both the e.max and quartz specimens, the Clearfil Photo Bond Universal with Clearfil Porcelain Bond Activator group had the highest pre- and post-thermocycling bond strength values. Combined use of silane in the acidic environment of a phosphate functional monomer and initiators enhances bond strength of a resin-based luting agent to e.max ceramic and quartz materials.
- 著者
- Futoshi KOMINE Shingo KAMIO Hiroki TAKATA Shogo YAGAWA Serina TAGUCHI Kohei TAGUCHI Akiko HASHIGUCHI Hideo MATSUMURA
- 出版者
- 日本歯科理工学会
- 雑誌
- Dental Materials Journal (ISSN:02874547)
- 巻号頁・発行日
- pp.2017-057, (Released:2017-09-07)
- 参考文献数
- 41
- 被引用文献数
- 3
This study evaluated the effect of zirconia framework design on fracture load of implant-supported zirconia-based prostheses after thermal cycling and mechanical loading. Three different zirconia framework designs were investigated: uniform-thickness (UNI), anatomic (ANA), and supported anatomic (SUP) designs. Each framework was layered with feldspathic porcelain (ZAC group) or indirect composite material (ZIC group). The specimens then underwent fracture load testing after thermal cycling and cyclic loading. In the ZAC group, mean fracture load was significantly lower for UNI design specimens than for the other framework designs. In the ZIC group, there was no significant difference in mean fracture load between ANA design specimens and either UNI or SUP design specimens. To improve fracture resistance of implant-supported zirconia-based prostheses after artificial aging, uniformly thick layering material and appropriate lingual support with zirconia frameworks should be provided.