This study aimed to evaluate the influence of surface pretreatment on the shear bond strength of resin luting cement to saliva-contaminated resin core foundation. The surface free energy (γS) of the adherent surfaces was examined. The two-way analysis of variance revealed that the surface pretreatment and storage conditions had a significant effect on the strength of the bond to resin core foundation. The γS values of the saliva-contaminated group were significantly lower than those of the other groups, and they tended to improve after surface pretreatment. The tendency of improvement in γS values differed depending on the type of pretreatment agents. Surface treatment with solutions containing functional monomers is effective in removing saliva contaminants from the resin core foundation surfaces and in creating an effective bonding surface for the resin luting cement.
- 著者
- Tatsuya IIJIMA Hiroyasu KUROKAWA Toshiki TAKAMIZAWA Eizo HIROKANE Nao TAKAHASHI Kengo WAKAMATSU Shunichi SUDA Masashi MIYAZAKI
- 出版者
- The Japanese Society for Dental Materials and Devices
- 雑誌
- Dental Materials Journal (ISSN:02874547)
- 巻号頁・発行日
- pp.2021-011, (Released:2021-06-30)
- 参考文献数
- 40
The purpose of this study was to investigate the ability of polishing paste containing surface pre-reacted glass-ionomer (S-PRG) filler to prevent acidic attack on tooth enamel surfaces. Resin composites were filled in the standardized cavities and finished with silicon carbide paper. These specimens were divided into three groups: the unpolished “control” group, the “PRG” group polished with S-PRG paste, and the “DDP” group polished with diamond-containing polishing paste. Following polishing, the specimens were immersed in a lactic acid buffer solution for 28 days. Optical coherence tomography (OCT) signals were measured to obtain the signal intensity and width at 1/e2 at selected locations on the enamel surface adjacent to the restoration. Although signal intensity significantly increased in all groups, widths at 1/e2 did not change significantly in the PRG group. For both the control and DDP groups, signal intensity and width at 1/e2 increased and decreased over time, respectively.
- 著者
- Shunichi SUDA Akimasa TSUJIMOTO Wayne W. BARKMEIER Kie NOJIRI Yuko NAGURA Toshiki TAKAMIZAWA Mark A. LATTA Masashi MIYAZAKI
- 出版者
- The Japanese Society for Dental Materials and Devices
- 雑誌
- Dental Materials Journal (ISSN:02874547)
- 巻号頁・発行日
- pp.2017-059, (Released:2017-11-23)
- 参考文献数
- 51
- 被引用文献数
- 20
The effect of phosphoric acid pre-etching on enamel bond fatigue durability of universal adhesives and two-step self-etch adhesives was investigated. Four universal adhesives and three two-step self-etch adhesives were used. The initial shear bond strengths and shear fatigue strengths to enamel with and without phosphoric acid pre-etching using the adhesives were determined. SEM observations were also conducted. Phosphoric acid pre-etching of enamel was found to increase the bond fatigue durability of universal adhesives, but its effect on two-step self-etch adhesives was material-dependent. In addition, some universal adhesives with phosphoric acid preetching showed similar bond fatigue durability to the two-step self-etch adhesives, although the bond fatigue durability of universal adhesives in self-etch mode was lower than that of the two-step self-etch adhesives. Phosphoric acid pre-etching enhances enamel bond fatigue durability of universal adhesives, but the effect of phosphoric acid pre-etching on the bond fatigue durability of two-step self-etch adhesives was material-dependent.
- 著者
- Chie KANAZAWA Ryosuke MURAYAMA Tetsuya FURUICHI Arisa IMAI Shunichi SUDA Hiroyasu KUROKAWA Toshiki TAKAMIZAWA Masashi MIYAZAKI
- 出版者
- 日本歯科理工学会
- 雑誌
- Dental Materials Journal (ISSN:02874547)
- 巻号頁・発行日
- pp.2016-175, (Released:2016-12-06)
- 参考文献数
- 28
This study used an ultrasonic measurement device to monitor the setting behavior of silicone elastomeric impression materials, and the influence of temperature on setting behavior was determined. The ultrasonic device consisted of a pulser-receiver, transducers, and an oscilloscope. The two-way transit time through the mixing material was divided by two to account for the down-and-back travel path; then it was multiplied by the sonic velocity. Analysis of variance and the Tukey honest significant difference test were used. In the early stages of the setting process, most of the ultrasonic energy was absorbed by the elastomers and the second echoes were relatively weak. As the elastomers hardened, the sonic velocities increased until they plateaued. The changes in sonic velocities varied among the elastomers tested, and were affected by temperature conditions. The ultrasonic method used in this study has considerable potential for determining the setting processes of elastomeric impression materials.