著者

小林 俊郎

出版者

社団法人 日本金属学会

雑誌

日本金属学会会報 (ISSN:00214426)

巻号頁・発行日

vol.27, no.8, pp.664-670, 1988-08-20 (Released:2011-08-10)

参考文献数

50

被引用文献数

3 1

著者

小林 俊郎 新家 光雄 稲垣 育宏

出版者

The Iron and Steel Institute of Japan

雑誌

鉄と鋼 (ISSN:00211575)

巻号頁・発行日

vol.75, no.3, pp.537-544, 1989-03-01 (Released:2010-01-18)

参考文献数

16

被引用文献数

1 1

---

It is highly expected that the ductility and toughness of titanium alloys bearing unstable β phase may be developed by the stress relaxation caused by strain-induced transformation. In this study, tensile test, Charpy impact test, static and dynamic fracture toughness tests were carried out at various temperatures on typical titanium alloys bearing unstable β phase. The strain-induced α″ martensitic transformation occurred in the (α+β) type Ti-6Al-2Sn-4Zr-6Mo alloy and the dynamic fracture toughness of this alloy increased considerably at 223 K. The strain-induced α' martensitic transformation occurred in the (α+β) type Ti-6Al-4V alloy, and the static and dynamic fracture toughness increased considerably at 123 and 223 K respectively and strength increased at low test temperatures in this alloy. The mechanical twin occurred in the β type Ti-15V-3Al-3Sn-3Cr alloy and the elongation of this alloy increased considerably at 123 K.

著者

新家 光雄 小林 俊郎 イゴール アレクセービッチアクモリン

出版者

一般社団法人 軽金属学会

雑誌

軽金属 (ISSN:04515994)

巻号頁・発行日

vol.42, no.11, pp.605-613, 1992-11-30 (Released:2008-10-30)

参考文献数

60

被引用文献数

2 6

著者

青山 正治 横井 時秀 小林 俊郎

出版者

公益社団法人 日本鋳造工学会

雑誌

鋳物 (ISSN:00214396)

巻号頁・発行日

vol.60, no.4, pp.240-245, 1988-04-25 (Released:2011-09-08)

参考文献数

11

被引用文献数

1

---

Spheroidal graphite cast irons containing four levels of Ni 0 to 3.5wt% and ones containing five levels of Mo 0 to 0.6wt% were prepared by the use of an induction furnace and cast. The iron into which Ni has been separately added has improved tensile strength and hardness because of solution hardening in the matrix. The impact transition temperature rises with condensation of Ni, while the upper shelf absorbed energy reduces. Separate addition of Mo has little effect on tensile strength and impact properties. Mechanical properties of spheroidal graphite cast iron can be improved by combined addition of Ni and Mo. The irons containing 1% Ni-0.1%Mo and 2.5%Ni-0.4%Mo show the lower impact transition temperature and have high toughness.

著者

戸田 裕之 山本 信 小林 正和 小林 俊郎 Qian Lihe 上杉 健太朗

出版者

社団法人日本材料学会

雑誌

学術講演会講演論文集

巻号頁・発行日

vol.56, pp.85-86, 2007-05-18

著者

高橋 志郎 新家 光雄 福井 壽男 小林 俊郎 長谷川 二郎

出版者

一般社団法人日本歯科理工学会

雑誌

歯科材料・器械 (ISSN:02865858)

巻号頁・発行日

vol.15, no.6, pp.577-584, 1996-11-25

被引用文献数

12

---

種々の熱処理を施した歯科用金銀パラジウム銅合金につき, 引張試験および動的破壊靱性試験を行い, 引張および衝撃破壊特性に及ぼす熱処理条件の影響について検討した.引張強さおよび0.2%耐力は, 溶体化まま材および溶体化時効材とも, ほぼ溶体化温度の上昇に伴い増加する傾向にある.溶体化時効材では, いずれの溶体化温度でも時効温度の上昇に伴い, 引張強さおよび0.2%耐力が増加する傾向にある.一方, 伸びは, 溶体化まま材では, 強度特性値とは逆に, 溶体化温度が高いほど低下する傾向にある.動的破壊靱性値は, 一部の例外を除き, 強度特性値の場合と同様に, 溶体化温度の上昇とともに増加する傾向にある.これは, 本合金の動的破壊靱性値に対して, 延性の低下に比べ, 強度の増加がより大きく寄与したためであると考えられる.動的破壊靱性値は, 溶体化まま材の方が溶体化時効材に比べ大きい.強度, 靱性, 延性バランスを考慮すると, 溶体化温度1073Kの熱処理条件がより適切である.特に, 溶体化まま材で, 溶体化後空冷の熱処理は, 冷却工程が簡便で, 時効工程を省略でき, より有利な熱処理条件といえる.