The fundamental experiment for the purpose of recovery of vanadium from oil burning ash, which was the valuable resources in Japan, was carried out. The following summarized the results.Sulfuric acid was superior to aqueous ammonia as extraction media in the process of leaching vanadium ion from oil burning ash.Precipitation ratio of vanadium compounds at room temperature was low. For example, the yield of vanadium compounds for 259200 s was no more than 60%. On the contrary, the precipitation rate increased at the higher reaction temperature and the yield reached up to approximately 100% at 80°C.Initial concentration of vanadium ion was the important factor besides pH and reaction temperature. The higher initial concentration of vanadium ion enlarged the appropriate pH range for the precipitation. In the case of 16000 ppm of the initial concentration, the pH range was 2.0 to 2.8. It was wider than that of 4000 ppm or 8000 ppm.The above results suggested that the higher initial concentration of vanadium ion, proper pH and higher reaction temperature were necessary to recover vanadium from oil burning ash efficiently.

著者

梅垣 高士 戸田 善朝 鈴木 喬 門間 英毅 安江 任 荒井 康夫

出版者

東京都立大学

雑誌

基盤研究(A)

巻号頁・発行日

1995

---

リン酸塩類の水和およびその生成物について、研究・調査を行い、下記のような成果を得た。1)ポルトランドセメントや石膏から得られる水和硬化体は、多孔体となるため、曲げ強度が充分でない。リン酸カルシウム類の水和硬化体も同じ欠点を持っているので、硬化体の密度を増加させることと水和生成物粒子同士の結合強度を増加させる目的で、水和反応時に水溶性の高分子化合物を添加して、硬化体の調製を行っている。現在のところ、硬化体の密度の増加は、十分でないものの、曲げ強度は、改善された。(梅垣高士,山下仁大)2)アパタイト水和硬化体を調製する際に、出発物質として、非晶質リン酸カルシウムの利用を試み、また、有機酸を添加してその効果をしらべた。(安江任、荒井康夫)3)骨生理学上重要な各種カチオンを共存させて水酸アパタイトを電析させて、その生成結晶について、詳細な検討を行った。(門間英毅)4)水酸アパタイトを無機イオン交換体への応用についての検討を行った。その結果、鉛、カドウミウムなどの有害イオンを除去できる可能性を認めた。(鈴木喬)5)コバルト、ニッケルなどのリン酸塩類水和物を合成し、顔料として応用の検討を行い、合成法は、簡便で、従来の顔料と比較しても遜色ないものが得られることを認めた。(戸田善朝)