In this study, hydrogen absorption behavior of steels on a vehicle during driving and parking in deicing-salt-spraying areas was investigated by using temperature-compensating hydrogen absorption monitoring system. During the driving of the vehicle in the areas, hydrogen permeation current of steel was increased due to picking up of salt water from the road when the road was wet. On the other hand, during the parking of the vehicle, the magnitude of the hydrogen permeation current were indicated that the hydrogen permeation current in the automobile driving environments is related to both driving states of a vehicle and environmental conditions such as temperature and relative humidity.

著者

多田 英司 西方 篤

出版者

公益社団法人 日本化学会

雑誌

化学と教育 (ISSN:03862151)

巻号頁・発行日

vol.65, no.12, pp.612-615, 2017-12-20 (Released:2018-06-01)

参考文献数

7

被引用文献数

1

---

金属の腐食反応は,金属のイオン化(酸化反応)と環境中の酸化剤の還元反応がカップルして進行する酸化還元反応である。本稿では,金属の腐食反応とその後の“さび”(腐食生成物)の形成過程について,鉄と銅を例にして概説する。

著者

西方 篤

出版者

東京工業大学

雑誌

基盤研究(A)

巻号頁・発行日

2008

---

耐候性鋼製のくし型プローブ電極を試作し、新潟市の苗引橋と福山市の両国橋(いずれも耐候性鋼橋梁)において、耐候性鋼の腐食モニタリングを2年間実施した。低周波数のインピーダンスの逆数1/Z_<10mH>の平均値は、腐食減量から得られた平均腐食速度Icorrと極めて高い相関を示し、相関式(Icorr/μAcm^<-2>)=17. 7×(Z10mHz/Ωcm^2)^<-0. 16>を得た。この相関式によりモニタリングデータから直接平均腐食速度を推定することが可能となった。