著者

青木 祥宏 黒岩 良祐 藤井 英俊 村山 元 泰山 正則

出版者

一般社団法人 日本鉄鋼協会

雑誌

鉄と鋼 (ISSN:00211575)

巻号頁・発行日

vol.103, no.7, pp.422-428, 2017 (Released:2017-06-30)

参考文献数

32

被引用文献数

17 11

---

Linear Friction Welding (LFW) is a solid-state joining process, in which a joint is obtained through the relative motion of two components under a high contact load. The most important factor of this conventional method is to obtain a fresh surface at the interface by expelling the weld interface as flash. In this study, medium carbon steel was welded by LFW at a low frequency, low amplitude and high applied pressure. As a result of the temperature measurements and microstructure observations, the maximum temperature of the weld plane was confirmed to be below the A1 transformation temperature, and martensitic transformation was prohibited at the weld interface. The key concept of this method are applying a large strain deformation to the interfaces to recrystallize at a lower temperature which is different from the conventional LFW.

著者

青木 祥宏 藤井 英俊

出版者

一般社団法人 溶接学会

雑誌

溶接学会全国大会講演概要

巻号頁・発行日

vol.2017, pp.282-283, 2017

---

線形摩擦接合(LFW)のこれまでの研究において、印加応力を増加させることで接合温度を低温化できることが、明らかとされてきた。本研究では、この現象をTi合金に適用し微細組織の観点から調査することで、βトランザス温度以下の接合温度で、Ti合金をLFWできることを実証する。

著者

高橋 誠司 青木 祥宏

出版者

社団法人溶接学会

雑誌

溶接学会誌 (ISSN:00214787)

巻号頁・発行日

vol.70, no.5, pp.568-569, 2001-07-05